Continuously Hot-Dip Coated Steel Flat Products
Continuously hot-dip flat rolled products | Aluminium-silicon alloy coated (+AS)

Continuously hot-dip flat rolled products | Aluminium-silicon alloy coated (+AS) | High strength steels

these products are characterised by guaranteed minimum yield, rupture and elongation limits.

They are coated products, which are ideal for cold forming, from bending to moulding, while maintaining high resistance values; they are suitable for obtaining resistant and resilient parts, in complex and lightened shapes, are their thicknesses can be reduced. They are widely used, for example, in the automobile and shelving sectors.

The tables below show only the main characteristics of the products listed and not all the technical supply conditions. For further details, please refer to the full contents of the standards mentioned on this page.


Condizioni tecniche di fornitura: EN 10346:2015

Tolleranze dimensionali e di forma: EN 10143:2006

CARATTERISTICHE MECCANICHE (Ved. note (*))

QUALITA’ Tipo
Rivestimento
CARATTERISTICHE MECCANICHE (Ved. note (*))
Re/ Rp0,2%
(Mpa)
Rm
(Mpa)
A%
min.
L0=80 mm
A%
min.
L0=80 mm
A%
min.
L0=80 mm
Spessore (S) 0,35<=S<=3,0 0,35<=S<=3,0 0,35<S<=0,5 0,5<S<=0,7 0,70<S<=3,0
HX260LAD +Z 260 – 330 350 – 430 22 24 26
HX260LAD +ZM, +AZ, +AS 260 – 330 350 – 430 20 22 24
HX300LAD +Z 300 – 380 380 – 480 19 21 23
HX300LAD +ZM, +AZ, +AS 300 – 380 380 – 480 17 19 21
HX340LAD +Z 340 – 420 410 – 510 17 19 21
HX340LAD +ZM, +AZ, +AS 340 – 420 410 – 510 15 17 19
HX380LAD +Z 380 – 480 440 – 560 15 17 19
HX380LAD +ZM, +AZ, +AS 380 – 480 440 – 560 13 15 17
HX420LAD +Z 420 – 520 470 – 590 13 15 17
HX420LAD +ZM, +AZ, +AS 420 – 520 470 – 590 11 13 15
HX460LAD +Z 460 – 560 500 – 640 11 13 15
HX460LAD +ZM, +AZ, +AS 460 – 560 500 – 640 9 11 13
HX500LAD +Z 500 – 620 530 – 690 9 11 13
HX500LAD +ZM, +AZ, +AS 500 – 620 530 – 690 7 9 11

 

(*) Si applica il provino (T) trasversale alla direzione di laminazione.

ANALISI CHIMICA COLATA (Valori % max.)

QUALITA’ Tipo
Rivestimento
ANALISI CHIMICA COLATA (Valori % max.)
C Mn Si P S Al Nb Ti
HX260LAD +Z, +ZM, +AZ, +AS 0,110 1,000 0,500 0,030 0,025 >=0,015 0,090 0,150
HX260LAD +ZM, +AZ, +AS 0,110 1,000 0,500 0,030 0,025 >=0,015 0,090 0,150
HX300LAD +Z 0,120 1,400 0,500 0,030 0,025 >=0,015 0,090 0,150
HX300LAD +ZM, +AZ, +AS 0,120 1,400 0,500 0,030 0,025 >=0,015 0,090 0,150
HX340LAD +Z 0,120 1,400 0,500 0,030 0,025 >=0,015 0,100 0,150
HX340LAD +ZM, +AZ, +AS 0,120 1,400 0,500 0,030 0,025 >=0,015 0,100 0,150
HX380LAD +Z 0,120 1,500 0,500 0,030 0,025 >=0,015 0,100 0,150
HX380LAD +ZM, +AZ, +AS 0,120 1,500 0,500 0,030 0,025 >=0,015 0,100 0,150
HX420LAD +Z 0,120 1,600 0,500 0,030 0,025 >=0,015 0,100 0,150
HX420LAD +ZM, +AZ, +AS 0,120 1,600 0,500 0,030 0,025 >=0,015 0,100 0,150
HX460LAD +Z 0,150 1,700 0,500 0,030 0,025 >=0,015 0,100 0,150
HX460LAD +ZM, +AZ, +AS 0,150 1,700 0,500 0,030 0,025 >=0,015 0,100 0,150
HX500LAD +Z 0,150 1,700 0,500 0,030 0,025 >=0,015 0,100 0,150
HX500LAD +ZM, +AZ, +AS 0,150 1,700 0,500 0,030 0,025 >=0,015 0,100 0,150

 

Legenda dei rivestimenti:

+Z= Rivestimento con lega di zinco, con contenuto in Zinco >=99%

+ZM= Rivestimento con lega di Alluminio, Zinco con contenuto tra l’1,5% e l’8%, con contenuto minimo di Magnesio dello 0,2% ed il resto Zinco.

+AZ= Rivestimento con lega di Alluminio, Silicio e zinco, con contenuto di Alluminio del 55%, di Silicio dell’1,6% ed il resto Zinco.

+AS= Rivestimento con lega di Alluminio e Silicio, con contenuto di Silicio dell’11% ed il resto Alluminio